CO2 is the primary cause of global warming. Alternative energy source should be provided without producing more CO2, such as solar energy. One of the best routes to remedy CO2 is to transform it to hydrocarbons using photo reduction. In our study, CO2 was photocatalytically reduced to produce methanol using a Hg lamp with wavelength 365 nm in a steady-state optical-fiber photo reactor. The optical-fiber photo reactor, comprised of near 120 Cu/TiO2-coated fibers, was designed and assembled to transmit and spread light uniformly inside reactor. TiO2 film was coated on optical fiber using dip-coating method. Titania and Cu-loaded solutions were prepared by a thermal hydrolysis method. The thickness of Cu/TiO2 film was 53 nm and consisted of very fine spherical particle with diameter of near 14 nm. The XRD spectra indicated the anatase phase of all TiO2 and Cu/TiO2 films. The wavelength of absorption edge was on 367 nm, equivalent to near 3.3 eV. Most active Cu species on TiO2 surface were Cu2O clusters, and played an important role for the formation of methanol. The methanol yield increased with UV irradiative intensity. Photo activity increased with increasing Cu loadings. Maximum methanol rate was 0.45 μmole/g-cat•hr using 1.2 wt%-Cu/TiO2 catalyst under 16 W / cm2 irradiation, 1.3 bar pressure of CO2, and 5000 seconds mean residence time. Higher than 1.2 wt% Cu loading gave less rate of methanol yield because of the masking effect of Cu2O clusters on the surface of TiO2."> 照片减少二氧化碳通过二氧化钛光催化剂甲醇 - raybet雷竞app,雷竞技官网下载,雷电竞下载苹果

国际期刊的Photoenergy

//文章

在这一页上

文摘版权

开放获取

体积 7 |文章的ID 324760年 | https://doi.org/10.1155/S1110662X05000176

杰弗里·c·s .吴Hung-Ming林, ”照片的减少有限公司 2 甲醇通过 TiO 2 光催化剂”,国际期刊的Photoenergy, 卷。7, 文章的ID324760年, 5 页面, 2005年。 https://doi.org/10.1155/S1110662X05000176

照片的减少有限公司 2 甲醇通过 TiO 2 光催化剂

杰弗里·c·s .吴¹和 Hung-Ming林¹

¹国立台湾大学化学工程系,10617年台北,台湾

文摘

等温室气体有限公司 2 是全球变暖的主要原因。应提供替代能源而不生产更多有限公司 2 ,比如太阳能。补救措施的最佳途径之一有限公司 2 减少使用的照片,将其转换为碳氢化合物。在我们的研究中, 有限公司 2 保留降低生产甲醇使用Hg灯与波长365 nm反应堆稳态光纤的照片。光纤照片反应堆,由120立方/附近 TiO 2 涂层纤维,设计并组装传输和扩散光反应器内均匀。 TiO 2 薄膜涂层在光纤采用浸涂法。二氧化钛和Cu-loaded解决方案是由热水解方法。铜的厚度/ TiO 2 电影是53海里,由非常细的球形颗粒直径接近14 nm。XRD结果表明所有的锐钛矿相 TiO 2 和铜/ TiO 2 电影。吸收边的波长367 nm,相当于3.3 eV附近。最活跃的铜物种 TiO 2 表面是铜 2 O 集群,甲醇的形成发挥了重要作用。甲醇产量增加,紫外线会发光的强度。活动照片铜载荷的增加而增加。最大的甲醇率为0.45 μ 摩尔/ g-cat • 使用1.2 wt %铜/人力资源 TiO 2 16岁以下的W /催化剂厘米 2 辐照,1.3酒吧的压力有限公司 2 平均停留时间,5000秒。高于1.2 wt %铜加载给少的甲醇产量的掩蔽效应铜 2 O 集群二氧化钛表面。

版权

版权©2005 Hindawi出版公司。这是一个开放的分布式下文章知识共享归属许可,它允许无限制的使用、分配和复制在任何媒介,提供最初的工作是正确引用。

PDF

下载引用

引用

订单打印副本订单

的观点770年

下载4930年

引用

文章奖:2020年杰出的研究贡献,选择由我们的首席编辑。获奖的文章阅读。